AbstractThe aim of this study was to manufacture a new zirconia implant (Y-TZP) and to evaluate the fracture strength and stresses generated after cyclic loading compared to titanium implants. Thirty-three zirconia and titanium implants were fabricated. The stress generated around the implants was observed by photoelastic analysis. The implants were then separated into groups (n = 10): Control (no treatment), mechanical fatigue and thermomechanical fatigue. All groups were submitted to a single cantilever flexure test to measure the material fracture strength. The results (2-way ANOVA, Bonferroni test, p <.05) showed no statistically significant difference in the stresses generated between the zirconia and titanium implants. Titanium implants showed higher fracture strength than the zirconia implants, a property that was not altered by fatigue applied. It was concluded that stress distribution was similar for Zr and Ti and mechanical and thermomechanical fatigue had no influence on the fracture strength of the implants tested.

O objetivo deste estudo foi avaliar estabilidade de cor de compósitos submetidos a diferentes períodos de envelhecimento artificial acelerado (EAA). Foram confeccionados, em matriz de teflon (10x2 mm), 24 corpos-de-prova de três compósitos (n=8): Tetric Ceram (Ivoclar/Vivadent); Filtek P90 e Z250 (3M ESPE), cor A3. Após fotoativação por 20 s (FlashLite 1401), polimento e leitura inicial de cor (espectrofotômetro PCB 687; BYK Gardner), os corpos-de-prova foram submetidos ao EAA (C-UV, Comexim), com ciclos de 8 h: 4 h de exposições a raios UV-B a 50°C e 4 h de condensação a 50°C. Ao final de cada ciclo, leituras de cor eram realizadas e quando o valor médio de ΔE atingisse índice ≥3,30, o ensaio era encerrado. Observou-se que Tetric Ceram apresentou alteração de ΔE igual a 3,33 já no primeiro ciclo de envelhecimento. Com Filtek P90 foram necessários dois ciclos de EAA (ΔE=3,60) e para Z250 quatro (ΔE=3,42). Observou-se que a cada ciclo ocorria diminuição na luminosidade de todas as amostras (ΔL). Concluiu-se que um curto período de EAA já é suficiente para que compósitos apresentem alteração de cor inaceitável clinicamente e que esta alteração é material dependente.

The aim of this study was to evaluate the color stability of composites subjected to different periods of accelerated artificial aging (AAA). A polytetrafluorethylene matrix (10 x 2 mm) was used to fabricate 24 test specimens of three different composites (n=8): Tetric Ceram (Ivoclar/Vivadent); Filtek P90 and Z250 (3M ESPE), shade A3. After light activation for 20 s (FlashLite 1401), polishing and initial color readout (Spectrophotometer PCB 687; BYK Gardner), the test specimens were subjected to AAA (C-UV; Comexim), in 8-h cycles: 4 h exposure to UV-B rays at 50°C and 4 h condensation at 50°C. At the end of each cycle, color readouts were taken and the test ended when the mean value of ΔE attained a level ≥3.30. Tetric Ceram presented alteration in ΔE equal to 3.33 in the first aging cycle. For Filtek P90 and Z250, two (ΔE=3.60) and four (ΔE=3.42) AAA cycles were necessary. After each cycle, there was a reduction of luminosity in all the samples (ΔL). It was concluded that a short period of AAA was sufficient to promote clinically unacceptable color alteration in composites, and that this alteration was material-dependent.

OBJECTIVE:The purpose of this study was to evaluate the effect of mouth rinse solutions on color stability, surface roughness and microhardness of two composite resins. MATERIAL AND METHODS: Fifty test specimens of each composite (Filtek Z250 and Z350; 3M ESPE) were made using a teflon matrix (12x2 mm). Color, surface roughness and Knoop microhardness baseline measurements of each specimen were made and specimens (n=10) were immersed in 5 mouth rinse solutions: G1: distilled water (control), G2: Plax Classic, G3: Plax alcohol-free; G4: Periogard, and G5: Listerine. Final measurements of color, roughness and microhardness were performed and the results submitted to statistical analysis (2-way ANOVA, Bonferroni ’s test; p<0.05). RESULTS: The most significant color change was observed for Z250 when immersed in Listerine (p<0.05). Z350 showed greater color change when immersed in Plax alcohol-free (p<0.05), but with no significant difference for Listerine (p>0.05). With regard to roughness, both composites showed significant changes when immersed in Listerine in comparison with Plax alcohol-free (p<0.05). Microhardness of Z350 was shown to be significantly changed when the composite was immersed in Plax alcohol-free (p<0.05). CONCLUSION: Composite changes depended on the material itself rather than the mouth rinse solution used.

The purpose of this study was to assess the radiopacity and microhardness of different types of resin-based composites (RBC - hybrid; microhybrid; flowable; cement and polyacid modified) before and after being submitted to artificial accelerated aging. Fifty specimens (7 mm in diameter and 2 mm thick) were fabricated, 10 for each material. The specimens were light-cured and submitted to radiopacity and microhardness tests. After obtaining initial radiopacity and microhardness values, the specimens were taken to the artificial accelerated aging, and new measurement of radiopacity and microhardness of the samples was performed. Data were submitted to statistical analysis (Student's t-test - p < 0.05). None of the materials studied showed changes in radiopacity after artificial accelerated aging. There was a significant decrease in microhardness for the microhybrid and polyacid-modified RBC´s. This study suggests that radiopacity remains unaltered after materials are submitted to artificial accelerated aging. Microhardness, however, may vary due to plasticization of the aged RBC matrix.